Coated Arc Welding Rod (for Soft Steel and 490-550 MPa Grade High-Tension Steel) NS-03Hi

Volume Discount

[Features]
· Reduces the amount of welding fumes generated and uses a lime-titania welding rod that absorbs little moisture to enable comfortable welding and stable, sharp arcs
· In addition, excellent re-arc performance, bead elongation, and slag peeling as well as minimal scattering of spatter increase welding efficiency

Part Number

Once your search is narrowed to one product,
the corresponding part number is displayed here.

Part Numbers

Data to be displayed: 30; 45; 60

Part Number
NSSW-NS-03HI-2.6-5
NSSW-NS-03HI-3.2-5
NSSW-NS-03HI-4-5
NSSW-NS-03HI-4-20

Standard Unit Price	Minimum order quantity	Volume Discount	Standard Shipping Days ?	Pole diameter (mm)	Pole length (mm)	Current range, lower (A)	Current range, vertical position, elevating, upper	Amount Of Content	Mass (g)
58.92 €	1	Available	9 Days	2.6	350	60–100	50～90/50～90	1 Box (5 kg)	5000
56.34 €	1	Available	9 Days	3.2	350	100~150	80～130/80～130	1 Box (5 kg)	5000
55.38 €	1	Available	13 Days	4	450	140~200	100～170/100～170	1 Box (5 kg)	5000
211.53 €	1	Available	7 Days	4	450	140~200	100～170/100～170	1 Box (20 kg)	20000

Basic information

Product Type	Welding rod	Tensile Strength(Mpa)	490	Stretch(%)	28
Yield Stress(Mpa)	435	Absorbed energy((0℃)J)	100	Features	Reduce the amount of welding fumes generated, and with a lime titanium welding rod, which resists absorbing moisture, a stable sharp arc can be welded comfortably. In addition, excellent re-arc performance, bead elongation, and slag peeling as well as minimal scattering of spatter increase welding efficiency.
Application	For welding medium plate of mild steel (SS400, SM400, etc.) for use in vehicles, building, and other general structures.	Main Points for Welding Construction	If the coating agent absorbs too much moisture, more fumes will be generated and the arc and slug will become unstable, resulting in increased spattering. In addition, the chances of undercutting and blow holes will also increase. Therefore, be sure to dry the material for about 60 minutes at 70°C-120°C. Welding with an excessive current or large weaving will reduce X-ray performance, always use an appropriate current. When using weaving, make sure to stay within 2.5 times the rod diameter.	Example of Deposited Metal Chemical Composition C(%)	0.07
Si(%)	0.17	Mn(%)	0.39	P(%)	0.015
S(%)	0.009	JIS Standard	Z 3211 E4303U	AWS Standard	A5.1 E6013 Applicable
Pole end color	Blue	Specifications	Lime-titania for general building welding

Configure

4Suggestion of an applicable part number.

View Part Numbers

Some specification is not specified yet.

The part number is completed.

Basic Attributes

Pole diameter(mm)
2.6

3.2

4
Clear
Pole length(mm)
350

450
Clear
Current range, lower(A)
60–100

100~150

140~200
Clear
Current range, vertical position, elevating, upper
50～90/50～90

80～130/80～130

100～170/100～170
Clear
Amount Of Content
- 1 Box (5 kg)
- 1 Box (20 kg)
Clear
Mass(g)
- 5000
- 20000
Clear
Type
- NSSW-NS-03HI
Clear