Hard Cladding MAG Material / Welding Wire DW-H700
Suitable for anti earth and sand abrasion. Contains Mo, V, and W, with negligible reductions in hardness even after heat treatment, enabling it to remain stable.
Part Number
Once your search is narrowed to one product,
the corresponding part number is displayed here.
DW-H700-1.2-20
Basic information
| Product Type | Welding wire | Wire Diameter(mm) | 1.2 | JIS Standard | Z3326 YF3B-C-600 |
|---|---|---|---|---|---|
| Amount Of Content | 1 winding (20 kg) | Mass(g) | 20000 | Application and Usage Characteristic | Suitable for anti earth and sand abrasion. Even after heat treatment, Mo, V, and W remain stable and the reduction in hardness is negligible. So it remains stable. |
| Chemical Composition of Deposited Metal B(%) | - | Chemical Composition of Deposited Metal C(%) | 0.57 | Chemical Composition of Deposited Metal Si(%) | 0.73 |
| Chemical Composition of Deposited Metal Mn(%) | 1.05 | Chemical Composition of Deposited Metal Cr(%) | 5.40 | Chemical Composition of Deposited Metal Mo(%) | 1.01 |
| Chemical Composition of Deposited Metal, Other | W:1.21 V:0.54 | Example of Weld Metal Hardness (Vickers Hardness) Welded State | 673 | Example of Weld Metal Hardness (Vickers Hardness) After Heat Treatment | 605 600℃×2h |
| Recommended preheating temperature and temperature between paths | 250 °C or More | Shield Gas | CO2 |
- The specifications and dimensions of some parts may not be fully covered. For exact details, refer to manufacturer catalogs .